[1]吴大军.采用烧结法制备微晶玻璃陶瓷板[J].华侨大学学报(自然科学版),2009,30(4):417-419.[doi:10.11830/ISSN.1000-5013.2009.04.0417]
　WU Da-jun.Prepration of the Microcrystal Glass-Ceramics by Sinter[J].Journal of Huaqiao University(Natural Science),2009,30(4):417-419.[doi:10.11830/ISSN.1000-5013.2009.04.0417]
点击复制

采用烧结法制备微晶玻璃陶瓷板()
分享到：

《华侨大学学报（自然科学版）》[ISSN:1000-5013/CN:35-1079/N]

卷:
第30卷
期数:
2009年第4期
页码:
417-419
栏目:
出版日期:
2009-07-20

文章信息/Info

Title:
Prepration of the Microcrystal Glass-Ceramics by Sinter
文章编号:
1000-5013(2009)04-0417-03
作者:
吴大军
华侨大学材料科学与工程学院
Author(s):
WU Da-jun
College of Material Science and Engineering, Huaqiao University, Quanzhou 362021, China
关键词:
微晶玻璃陶瓷;  辊道窑;  烧结法;  烧成制度
Keywords:
microcrystal glass-ceramics;  roller furnace;  sinter;  sintering system
分类号:
TQ171.733
DOI:
10.11830/ISSN.1000-5013.2009.04.0417
文献标志码:
A
摘要:
把天然矿物原料长石、石英和双飞粉、碳酸钡、氧化锌等粉料混匀,然后在熔块窑炉中熔融成玻璃液.经水淬,筛分成具有一定粒级的碎粒,干燥后置于模具中压实、压平,于辊道窑中晶化烧结成微晶玻璃陶瓷板.同样,也可以把上述熔块小颗粒用布料器在素坯上布料,经滚筒把熔块压平、压实,然后进辊道窑晶化,烧结成微晶玻璃陶瓷.制成的微晶玻璃陶瓷板产品的莫氏硬度为6.5,光泽度为98 Gs(光泽单位)以上,抗弯曲强度为31.4 MPa,抗压强度为450 MPa,吸水率为0.1%,具有耐急冷急热、耐酸碱、耐污染的能力.
Abstract:
The powders of natural minerals and precessing ingredient including feldspar,quartz,calcium carbonate,barium carbonate,zinc oxide were mixed together,and were melted into glass liquid in smelting furnace.After being treated by water,the dried glass substances of small pellet were shaped in a model,and then were sintered into microcrystal glass-ceramics in roller furnace.Its hardness strength,luster strength,resistance against winding strength,resistance against pressure strength and water absorption partcularly are 6.5,98 Gs,31.4 MPa,450 MPa and 0.1%,respectively.It possess good resistance against quick cooling and heating and heat,acid-alkuli surroundings,and pollution.

参考文献/References:

[1] 王文娟, 戚凭, 李延强. 陶瓷/微晶玻璃复合材料耐磨性的研究 [J]. 青岛大学学报(自然科学版), 2005(1):53-57.doi:10.3969/j.issn.1006-1037.2005.01.013.
[2] DONG Guo-ping, TAO Hai-zheng, XIAO Xiu-di. Second harmonic generation in transparent microcrystalline α-CdGa2S4-containing chalcogenide glass ceramics [J]. Optics Communications, 2007(2):466-470.doi:10.1016/j.optcom.2007.02.047.
[3] CHEN G J, JIAN L Y, CHANG Y S, el at. Preparation and properties of barium ferrite microcrystal in B2O3-Bi2O3 glass [J]. Journal of Crystal Growth, 2005, (1/4):457-461.doi:10.1016/j.jcrysgro.2004.12.183.
[4] TANAKA K, HIRAO K, SOGA N. Preparation magnetic properties of glass-ceramics containing magnetite microcrystals in calcium iron aluminoborate system [J]. Journal of Magnetism and Magnetic Materials, 1997, (1/2):203-212.
[5] CHEN G J, LEE H M, CHANG Y S, el at. Preparation and properties of yttrium iron garnet microcrystal in P2O5-MgO glass [J]. Jurnal of Alloys and Compounds, 2005(2):297-302.
[6] 毛必明. 新型建材--微晶玻璃板材的制造及展望 [J]. 陶瓷研究, 1996(4):199-200.
[7] 俞平利, 马拴锁. 山西翼城高炉渣在微晶玻璃中的应用 [J]. 华侨大学学报（自然科学版）, 2008(1):17-21.

更新日期/Last Update: 2014-03-23