[1]张敬阳,赵煌,吴伟端.高径厚比超细改性绢云母鳞片的研制[J].华侨大学学报(自然科学版),2005,26(1):51-53.[doi:10.3969/j.issn.1000-5013.2005.01.013]
　Zhang Jingyang,Zhao Huang,Wu Weiduan.Development of Ultrafine Modified Sericite Slice with Higher Diameter-Thickness Ratio[J].Journal of Huaqiao University(Natural Science),2005,26(1):51-53.[doi:10.3969/j.issn.1000-5013.2005.01.013]
点击复制

高径厚比超细改性绢云母鳞片的研制()
分享到：

《华侨大学学报（自然科学版）》[ISSN:1000-5013/CN:35-1079/N]

卷:
第26卷
期数:
2005年第1期
页码:
51-53
栏目:
出版日期:
2005-01-20

文章信息/Info

Title:
Development of Ultrafine Modified Sericite Slice with Higher Diameter-Thickness Ratio
文章编号:
1000-5013(2005)01-0051-03
作者:
张敬阳; 赵煌; 吴伟端
华侨大学材料科学与工程学院; 华侨大学材料科学与工程学院 福建泉州362021; 福建泉州362021; 福建泉州362021
Author(s):
Zhang Jingyang;  Zhao Huang;  Wu Weiduan
College of Material Science and Engineering, Huaqiao University, 362021, Quanzhou, China
关键词:
绢云母鳞片;  径厚比;  超细粉碎;  表面化学改性;  尼龙6
Keywords:
sericite slice;  diameter-thichness ratio;  ultrafine crashing;  surface chemical modification;  nylon 6
分类号:
TD985
DOI:
10.3969/j.issn.1000-5013.2005.01.013
文献标志码:
A
摘要:
采用超音速气流粉碎方法对绢云母进行超细粉碎,通过控制进口压力、工作压力和进料速度可生产出不同粒度、径厚比的绢云母超细粉 (鳞片 ) .采用硅烷偶联剂对超细绢云母进行表面化学改性,通过对径厚比、改性绢云母填充量等变量的研究,探讨改性绢云母增强尼龙 6力学性能的变化规律 .实验结果表明,高径厚比改性绢云母增强尼龙 6的力学性能有显著的提高 .
Abstract:
The ultrafine sericite powder (slice) with different size and diameter thickness ratio can be produced by adopting supersonic airflow crashing and by controlling entrance pressure and working pressure and feeding speed. The surface chemical modification of ultrafine sericite was carried out by using silane coupling agent. Such variables as diameter thickness ratio and filling amount of modified sericite were investigated. The regular pattern of the change of capacity of modified sericite in strengthening mechanical performance of nylon 6 was explored. As shown by experimental results, the capacity of modified sericite with higher diameter thickness ratio in strengthening nylon 6 is improved significantly.

参考文献/References:

[1] 丁浩, 邹蔚蔚. 中国绢云母资源综合利用的现状与前景 [J]. 中国矿业, 1996(4):14-18.
[2] 王经武. 塑料改性技术 [M]. 北京:化学工业出版社, 2004.717-719.
[3] 李冷. 机械力化学理论及实验方法 [J]. 国外非金属选矿, 1991(3):36-43.
[4] 吴季怀, 张敬阳, 魏从容. 天然矿物的深加工及其在橡塑弹性体中的应用 [J]. 华侨大学学报(自然科学版), 1997(4):373-376.
[5] Hokkaido J M. Surface modification power technology handbook [M]. London:Butterworths, 1994.453-457.
[6] 郑水林. 粉体表面改性 [M]. 北京:中国建材工业出版社, 1995.95-102.
[7] 罗谷风. 基础结晶学与矿物学 [M]. 南京:南京大学出版社, 1993.245-252.

备注/Memo

备注/Memo:
福建省自然科学基金资助项目(E0110024)
更新日期/Last Update: 2014-03-23